Nguzogide waya NiCr8020 / nichrome alloy / ni80cr20 waya nicr alloy waya
Nikrothal8, MWS-650,NiCrA, Tofet A, HAI-NiCr 80,Chromel A, Alloy A, Alloy 650, N8, Resistohm 80, Stablohm 650, Nichorme V, Nikrothal 80.
Ni80Cr20 bụ nickel-chromium alloy (NiCr alloy) mara elu resistivity, ezigbo oxidation resistance na ezigbo ụdị kwụsie ike.Ọ dị mma maka iji ya na okpomọkụ ruo 1200 Celsius, ma jide ndụ ọrụ dị elu ma e jiri ya tụnyere ígwè chromium alumium alloys.
Ngwa a na-ahụkarị maka Ni80Cr20 bụ ihe ndị na-ekpo ọkụ eletrik na ngwa ụlọ, ọkụ ụlọ ọrụ na ndị na-emegide (wirewound resistors, metal film resistors), igwe anaghị agba nchara, igwe igwe, igwe na-ekpo ọkụ mmiri, ịkpụzi plastik na-anwụ, ígwè na-ere ọkụ, ihe na-ekpuchi ígwè na ihe ndị na-emepụta ihe na cartridge.
Ngwakọta nkịtị%
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Ndị ọzọ |
Oke | |||||||||
0.03 | 0.02 | 0.015 | 0.60 | 0,75-1.60 | 20.0-23.0 | Bal. | Kachasị 0.50 | Kachasị 1.0 | - |
Njirimara arụrụ arụ (1.0mm)
Mpụta ike | Ike ọdụdọ | Ogologo oge |
Mpa | Mpa | % |
420 | 810 | 30 |
Njirimara anụ ahụ ahụkarị
Njupụta (g/cm3) | 8.4 |
Igwe ọkụ eletrik na 20ºC (Om * mm2 / m) | 1.09 |
Ọnụọgụ arụmọrụ na 20ºC (WmK) | 15 |
Ọnụọgụ nke mgbasawanye thermal | |
Okpomọkụ | Ọnụọgụ nke Mgbasa ọkụ x10-6/ºC |
20 ºC-1000ºC | 18 |
Kpọmkwem ike okpomọkụ | |
Okpomọkụ | 20ºC |
J/gK | 0.46 |
Ebe mgbaze (ºC) | 1400 |
Oke okpomọkụ na-aga n'ihu na ikuku (ºC) | 1200 |
Njirimara magnetik | na-abụghị magnetik |
Ihe Ndị Na-akpata Okpomọkụ nke Nguzogide Eletriki | |||||
20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 600ºC |
1 | 1.006 | 1.012 | 1.018 | 1.025 | 1.018 |
700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1300ºC |
1.01 | 1.008 | 1.01 | 1.014 | 1.021 | - |
Ụdị nke ọkọnọ
Aha Alloys | Ụdị | Akụkụ | ||
OhmAlloy109W | Waya | D=0.03mm~8mm | ||
OhmAlloy109R | Ribọn | W = 0.4 ~ 40mm | T = 0.03 ~ 2.9mm | |
OhmAlloy109S | Mwepu | W=8 ~ 250mm | T = 0.1 ~ 3.0mm | |
OhmAlloy109F | Foil | W=6 ~ 120mm | T = 0.003 ~ 0.1mm | |
OhmAlloy109B | Ogwe | Dia=8 ~ 100mm | L=50 ~ 1000mm |