Kan-thal APM FECral Alloys Igwe ọkụ na-eguzogide okpomọkụ dị elu

Nkọwa dị mkpirikpi:

Ngwaahịa a na-ewe ezigbo alloy a nụchara anụcha dị ka akụrụngwa, na-eji teknụzụ metallurgy ntụ ntụ na-emepụta alloy ingots, a na-arụpụta ya site na nhazi oyi na ọkụ pụrụ iche na usoro ọgwụgwọ okpomọkụ.Ngwaahịa ahụ nwere uru nke nguzogide oxidation siri ike, ezigbo nguzogide corrosion na oke okpomọkụ, obere ihe na-akpụ akpụ nke electro-thermal components, ogologo ndụ ọrụ na nnukwu okpomọkụ na obere mgbanwe nke nguzogide.Ọ dabara maka oke okpomọkụ 1420 C, ike dị elu, ikuku na-emebi emebi, ikuku carbon na gburugburu ọrụ ndị ọzọ.Enwere ike iji ya na kiln seramiiki, ọkụ ọgwụgwọ okpomọkụ dị elu, ọkụ ụlọ nyocha, ọkụ ụlọ ọrụ eletrik na ọkụ mgbasa.


  • Ụdị NO.:APM
  • Ngwa:ụlọ ọrụ
  • Ngwungwu njem:Akpa osisi
  • Nguzogide:1.45
  • Mmalite:Shanghai
  • Dayameta:0.05mm Min.
  • Nkọwa ngwaahịa

    FAQ

    Mkpado ngwaahịa

    1 (Wt%)isi mejupụtara

    C

    Si

    Mn

    Cr

    Al

    Fe

    Min

    -

    -

    -

    20

    5.5

    Bal.

    Oke

    0.04

    0.5

    0.4

    22

    6.0

    Bal.

     

    2Isi ihe eji arụ ọrụ

    Ike nkwụsịtụ na okpomọkụ ụlọ: 650-750MPa

    Ọnụego mgbanwe: 15-25%

    ike: HV220-260

    Ike tensile na 1000 ℃ Okpomọkụ 22-27MPa

    Ogologo oge dị elu na okpomọkụ 1000 na 6MPa ≥100h

    3.Njirimara anụ ahụ isi

    njupụta 7.1g / cm3

    resistivity 1.45×10-6 Ω.m

    Ọnụọgụ okpomọkụ na-eguzogide(Ct)

    800 ℃

    1000 ℃

    1400 ℃

    1.03

    1.04

    1.05

    Nkezi ọnụọgụ mgbasawanye ahịrị()

    20-800 ℃

    20-1000 ℃

    20-1400 ℃

    14

    15

    16

    ebe agbaze:Okpomọkụ na-aga n'ihu na-arụ ọrụ kacha 1400 ℃

    4Ndụ ngwa ngwa

    1300 ℃

    1350 ℃

     

    Nkezi ndụ ngwa ngwa (awa)

    110

    90

     

    Ọnụego mgbawa mgbe mgbawa gasịrị

    8

    11