23.00 Cr, 5.00 Al, Bal.Fe
Okpomọkụ na-arụ ọrụ nke ukwuu: 1250ºC.
Okpomọkụ na-agbaze: 1500ºC
Nguzogide eletriki: 1.35 ohm mm2/m
A na-ejikarị ụdị waya fecral alloy a eme ihe dị ka ihe na-ekpo ọkụ n'ọkụ ụlọ ọrụ na ọkụ eletrik.
O nwere obere ọkụ karia Alloys Tophet mana ebe mgbaze dị elu.
Ụlọ ọrụ SHANGHAI TANKII ALLOY MATERIAL CO., LTD
FECRAL NA ALCHROME ALOY PRODUCER NA CHINA, Ọkachamara Ọkachamara n'ụwa.
Nkọwapụta:
Ụdị Alloy | Dayameta | Nguzogide | Mgbatị | Ogologo oge (%) | Na-ehulata | Oke. Na-aga n'ihu | Na-arụ ọrụ Ndụ |
(mm) | (μΩm)(20°C) | Ike | Oge | Ọrụ | (awa) | ||
(N/mm²) | Okpomọkụ (°C) | ||||||
Cr20Ni80 | <0.50 | 1.09± 0.05 | 850-950 | >20 | >9 | 1200 | > 20000 |
0.50-3.0 | 1.13 ± 0.05 | 850-950 | >20 | >9 | 1200 | > 20000 | |
> 3.0 | 1.14± 0.05 | 850-950 | >20 | >9 | 1200 | > 20000 | |
Cr30Ni70 | <0.50 | 1.18± 0.05 | 850-950 | >20 | >9 | 1250 | > 20000 |
≥0.50 | 1.20± 0.05 | 850-950 | >20 | >9 | 1250 | > 20000 | |
Cr15Ni60 | <0.50 | 1.12± 0.05 | 850-950 | >20 | >9 | 1125 | > 20000 |
≥0.50 | 1.15± 0.05 | 850-950 | >20 | >9 | 1125 | > 20000 | |
Cr20Ni35 | <0.50 | 1.04± 0.05 | 850-950 | >20 | >9 | 1100 | > 18000 |
≥0.50 | 1.06 ± 0.05 | 850-950 | >20 | >9 | 1100 | > 18000 | |
1Cr13Al4 | 0.03-12.0 | 1.25± 0.08 | 588-735 | >16 | > 6 | 950 | > 10000 |
0Cr15Al5 | 1.25± 0.08 | 588-735 | >16 | > 6 | 1000 | > 10000 | |
0Cr25Al5 | 1.42± 0.07 | 634-784 | >12 | >5 | 1300 | >8000 | |
0Cr23Al5 | 1.35±0.06 | 634-784 | >12 | >5 | 1250 | >8000 | |
0Cr21Al6 | 1.42± 0.07 | 634-784 | >12 | >5 | 1300 | >8000 | |
1Cr20Al3 | 1.23 ± 0.06 | 634-784 | >12 | >5 | 1100 | >8000 | |
0Cr21Al6Nb | 1.45± 0.07 | 634-784 | >12 | >5 | 1350 | >8000 | |
0Cr27Al7Mo2 | 0.03-12.0 | 1.53± 0.07 | 686-784 | >12 | >5 | 1400 | >8000 |