FECral 0Cr15Al5 alloy eguzogide warara site factory
Fecral0Cr15Al5alloy iguzogide warara site factory
| Ọkwa | 0Cr15Al5 |
| Nha | ọkpụrụkpụ: 0.05-3mm obosara: 4-250mm |
| Elu | na-egbuke egbuke sliting |
| Ibu | 5-200kg / mpịakọta, dị ka ndị ahịa' ibu |
| Nguzogide | 1.3±0.05μΩ.m |
| Isi ike (HV) | 180-210HV |
| Ogologo oge | ≥16% |
| Ọkwa | Ọnọdụ okpomọkụ kachasị elu | Nguzogide | Isi ike | Ike ọdụdọ | Ogologo oge |
| 0Cr13Al4 | 1050 ℃ | 1.25±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr15Al5 | 1100 ℃ | 1.3±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr21Al6Nb | 1300 ℃ | 1.42±0.05μΩ.m | 200-240HV | 750N/mm2 | ≥12 |
| Cr20Ni80 | 1200 ℃ | 1.09±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr15Ni60 | 1150 ℃ | 1.12±0.05μΩ.m | 175-210HV | 750N/mm2 | ≥20 |
| Cr20Ni35 | 1100 ℃ | 1.04±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr25Ni20 | 1100 ℃ | 0.86±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Ọkwa | Ngwakọta kemịkalụ% | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| ≤ | |||||||||
| 0Cr15Al5 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | itule |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | itule |
| 0Cr13Al4 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | itule |
| Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | itule | 0.5 | ≤1.0 |
| Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | 0.5 | itule |
| Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | - | itule |
| Cr25Ni20 | 0.08 | 0,045 | 0.03 | 2.0 | 0.4-0.6 | 24-26 | 19-22 | - | itule |
Ụgwọ nke ụlọ ọrụ Shanghai Tankii Alloy Material Co., Ltd.ilekwasị anya na mmepụta nke nichrome alloy, thermocouple waya, fecral alloy, nkenke alloy, ọla kọpa nickel alloy, thermal ịgba alloy wdg n'ụdị waya, mpempe akwụkwọ, teepu, warara, mkpanaka na efere.
Anyị na-ama nwetara ISO 9001 àgwà usoro akwụkwọ na ihu ọma nke ISO 14001 gburugburu ebe obibi nchebe system.We nwe a zuru ezu set nke elu mmepụta eruba nke refining, oyi mbelata, ịbịaru na okpomọkụ ọgwụgwọ wdg Anyị na-anya isi nwere onwe R & D ikike.
Dee ozi gị ebe a ziga anyị ya