Dia 0.6mm Alloy M25 ọla kọpa Beryllium wires maka kọntaktị àkwà mmiri
Nkọwa ngwaahịa
Ngwakọta kemịkalụ (pasent ibu) nkeC17200 Beryllium ọla kọpa Alloy:
| Ngwọta na-enyefe | ||||||
| Alloy | Beryllium | Cobalt | Nickel | Co + Ni | Co+Ni+Fe | Ọla kọpa |
| C17200 | 1.80-2.00 | - | 0.20 min | 0.20 min | 0.60 Max | Nhazi |
Nkwuputa: ọla kọpa gbakwunyere mgbakwunye nhata 99.5% Min.
TNjirimara Anụ ahụ nkịtị nke C172:
Njupụta (g/cm3): 8.36
Njupụta tupu afọ ike (g/cm3): 8.25
Modul na-agbanwe (kg/mm2 (103): 13.40
Ọnụego Mgbasawanye okpomọkụ (20 °C ruo 200 °C m/m/°C): 17 x 10-6
Nrụpụta ọkụ (cal/(cm-s-°C): 0.25
Oke agbaze (°C): 870-980
Iwe nkịtị anyị na-enye:
| Nkọwapụta CuBeryllium | ASTM | Ngwa igwe na eletriki nke ọla kọpa Beryllium Strip | ||||||
| Nhọpụta | Nkọwa | Ike ọdụdọ (Mpa) | Mpụta Ike 0.2% akwụ ụgwọ | Pasent elongation | Ike (HV) | Ike Rockwell B ma ọ bụ C | Igwe ọkụ eletrik (% IACS) | |
| A | TB00 | Ngwọta ewepụrụ | 410-530 | 190-380 | 35-60 | <130 | 45-78HRB | 15-19 |
| 1/2 H | TD02 | Ọkara siri ike | 580-690 | 510-660 | 12-30 | 180-220 | 88-96HRB | 15-19 |
| H | TD04 | siri ike | 680-830 | 620-800 | 2 ~ 18 | 220-240 | 96-102HRB | 15-19 |
| HM | TM04 | Mill gbasiri ike | 930-1040 | 750-940 | 9-20 | 270-325 | 28-35HRC | 17-28 |
| SHM | TM05 | 1030-1110 | 860-970 | 9-18 | 295-350 | 31-37HRC | 17-28 | |
| XHM | TM06 | 1060-1210 | 930-1180 | 4 ~ 15 | 300-360 | 32-38HRC | 17-28 | |
Isi teknụzụ nke Beryllium ọla (Ọgwụgwọ okpomọkụ)
Ọgwụgwọ okpomọkụ bụ usoro kachasị mkpa maka usoro alloy a.Ọ bụ ezie na alloys ọla kọpa niile na-esi ike site na ịrụ ọrụ oyi, ọla kọpa beryllium bụ ihe pụrụ iche na-esi ike site na ọgwụgwọ okpomọkụ dị ala dị ala.Ọ na-agụnye nzọụkwụ abụọ bụ́ isi.Nke mbụ ka a na-akpọ mgbakasị ngwọta na nke abụọ, mmiri ozuzo ma ọ bụ ike afọ.
Ngwọta Annealing
Maka ụdị alloy CuBe1.9 (1.8- 2%) a na-ekpo ọkụ n'etiti 720°C na 860°C.N'ebe a beryllium dị n'ime na-agbaze n'ezie na matriks ọla kọpa (alpha phase).Site na imenyụ ngwa ngwa ruo n'ime ụlọ, a na-edobe usoro ihe ngwọta siri ike.Ihe dị n'oge a dị nnọọ nro ma dị nro ma nwee ike ịrụ ọrụ ngwa ngwa oyi site na ịse, ịkpụgharị mpịakọta, ma ọ bụ isi oyi.Arụ ọrụ mgbakasị ihe ngwọta bụ akụkụ nke usoro a na-eme n'igwe igwe ma ọ bụghị onye ahịa na-eji ya eme ihe.Okpomọkụ, oge na okpomọkụ, ọnụ ọgụgụ nkwụsị, nha ọka, na isi ike bụ ihe dị oke egwu ma TANKII na-achịkwa ya nke ọma.
Ịdị ike afọ
Ịgba ike afọ na-eme ka ike ihe dịkwuo elu nke ukwuu.A na-eme mmeghachi omume a na okpomọkụ n'etiti 260 ° C na 540 ° C dabere na alloy na njirimara achọrọ.Ọkpụkpụ a na-eme ka beryllium gbazere gbasasịa dị ka oge beryllium bara ụba (gamma) na matriks na n'ókè ọka.Ọ bụ nhazi nke mkpọda a na-eme ka mmụba dị ukwuu na ike ihe.A na-ekpebi ọkwa nke ihe eji arụ ọrụ site na okpomọkụ na oge na okpomọkụ.Ekwesịrị ịmara na ọla kọpa beryllium enweghị njirimara ịka nká nke ụlọ.