China 0Cr25Al5 / Kant-hal A / alloy 835/KA FECral alloy / Heating Waya / Furnace Spiral Heating Wire Manufacture and Factory |TANKII

0Cr25Al5/Kant-hal A/alloy 835/KA FECral alloy/Heating Waya/Fernace Spiral Heating Wire egosipụtara

0Cr25Al5/Kant-hal A/alloy 835/KA FECral alloy/Heating Waya/Firnace Spiral Heating Waya

Nkọwa dị mkpirikpi:

aha nlereanya:0Cr25Al5

ngwa:kpo oku

ihe:Fecral

elu:na-egbuke egbuke/oxidation

udi:gburugburu ma ọ bụ warara

Zitere anyị email

Nkọwa ngwaahịa

FAQ

Mkpado ngwaahịa

0Cr25Al5 FECral alloy/Heating Waya/Firnace Spiral Heating Waya

1. Nkọwa
Site na njirimara nke nguzogide dị elu, ọnụọgụ dị ala nke nguzogide eletriki, Igwe ọkụ na-arụ ọrụ dị elu, nguzogide corrosion dị mma n'okpuru okpomọkụ dị elu.
A na-ejikarị ya na locomotive eletriki, diesel locomotive, ụgbọ ala metro na ụgbọ ala na-akpụ akpụ dị elu wdg sistemu breeki resistor, seramiiki eletriki, ọkụ ụlọ ọrụ.

2. Nkọwapụta
1).Ihe mgbochi locomotive:
Ọkpụrụkpụ: 0.6mm-1.5mm
Obosara: 60mm-90mm

2).Eriri ihe na-eguzogide seramiiki seramiiki:
Ọkpụrụkpụ: 0.04mm-1.0mm
Ogologo: 5mm-12mm
Ọkpụrụkpụ & Obosara: (0.04mm-1.0mm)× 12mm(n'elu)

3).Rịbọn nguzogide dị ala:
Ọkpụrụkpụ & Obosara: (0.2mm-1.5mm)*5mm

4).Igwe ọkụ ụlọ ọrụrịbọn:
Ọkpụrụkpụ: 1.5mm-3.0mm
Obosara: 10mm-30mm

3. Atụmatụ
arụmọrụ kwụsiri ike;Anti-oxidation;Nguzogide corrosion;Nkwụsi ike dị elu nke okpomọkụ;Ikike ịkpụ ụdọ mmiri dị mma;Uniform na ọmarịcha ọnọdụ elu na-enweghị ntụpọ.

4. Nkwakọ ngwaahịa
Spool, eriri igwe, akpa osisi (dị ka onye ahịa chọrọ)

5. Ngwaahịa na ọrụ
1).ngafe: ISO9001 asambodo, na SO14001cetification;
2).Ezigbo ọrụ ire ere;
3).A nabatara obere usoro;
4).Ngwongwo kwụsiri ike na oke okpomọkụ;
5).nnyefe ngwa ngwa;

C	P	S		Mn		Si	Cr	Ni	Al	Fe	Ndị ọzọ
Oke
0.12	0.025		0.025		0.70	Kachasị 1.0	13.0-15.0	Kachasị 0.60	4.5-6.0	Bal.	-

Ihe eji arụ ọrụ

Oke ọrụ na-aga n'ihu	980ºC
Resistivity na 20ºC	1.28 ohm mm2/m
Njupụta	7.4 g/cm3
Nrụpụta okpomọkụ	52.7 KJ/m@h@ºC
Ọnụọgụ nke Thermal Mgbasawanye	15.4×10-6/ºC
Ebe mgbaze	1450ºC
Ike ọdụdọ	637~784 Mpa
Ogologo oge	Nkeji 12%
Ọnụego Mbelata Mgbanwe nke ngalaba	65 ~ 75%
Na-ehulata ugboro ugboro	Nkeji ugboro 5
Oge ọrụ na-aga n'ihu	-
Isi ike	200-260HB
Ọdịdị Micrographic	Ferrite
Ihe onwunwe magnetik	Magnetik

Ihe na-akpata okpomọkụ nke nguzogide eletrik

20ºC	100ºC	200ºC	300ºC	400ºC	500ºC	600ºC	700ºC	800ºC	900ºC	1000ºC
1	1.005	1.014	1.028	1.044	1.064	1.090	1.120	1.132	1.142	1.150

Nkọwa nkwakọ: nkọwa nnyefe:

Nguzogide kpo oku 0Cr25AL5 nkọwa nkwakọ waya: Plastic / spool, katọn, osisi osisi, akpa

Nwee ngwaahịa & nnyefe nguzogide kpo oku 0Cr25AL5 waya

Nkọwapụta

0Cr25AL5 FeCrAl na-eguzogide waya kpo oku
1.Fe-Cr-Al alloy
2.GB/T 1234-95
3.Anti-oxidation
0Cr25AL5 FeCrAl na-eguzogide waya kpo oku
Iron-chromium-aluminium (FeCrAl) alloys
FeCrAl alloys ji magburu onwe ọxịdashọn eguzogide na nnọọ mma ụdị kwụsie ike n'ihi na ogologo mmewere life.They na-a na-eji eletriki kpo oku ọcha ke ulo oru oku oku na ulo ngwa.

FeCrAl alloys nwere elu ọrụ okpomọkụ mgbe NiCr Alloys na ọtụtụ ala prices.Ma ha nwere ala kwụsie ike na mgbanwe, mfe na-emebi emebi mgbe oge okirikiri.

Isi akara ule na akụrụngwa

akara ule Njirimara		1Cr13Al4	0Cr25Al5	0Cr21Al6	0Cr23Al5	0Cr21Al4	0Cr21Al6Nb	0Cr27Al7Mo2
Ngwakọta kemịkalụ%	Cr	12.0-15.0	23.0-26.0	19.0-22.0	22.5-24.5	18.0-21.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	4.5-6.5	5.0-7.0	4.2-5.0	3.0-4.2	5.0-7.0	6.0-7.0
	Fe	Nhazi	Nhazi	Nhazi	Nhazi	Nhazi	Nhazi	Nhazi
	Ndị ọzọ						Nb 0.5	Mo1.8-2.2
Okpomọkụ ọrụ kacha elu °C		950	1250	1250	1250	1100	1350	1400
ResistivityμΩ.M,20°C		1.25	1.42	1.42	1.35	1.23	1.45	1.53
Njupụta (g/cm3)		7.4	7.10	7.16	7.25	7.35	7.10	7.10
Nrụpụta ọkụ KJ/mH Celsius		52.7	46.1	63.2	60.2	46.9	46.1	45.2
Ọnụọgụ nke linear extensibility Α×10-6/°C		15.4	16.0	14.7	15.0	13.5	16.0	16.0
Ebe mgbaze °C		1450	1500	1500	1500	1500	1510	1520
Mpa nhịahụ		580-680	630-780	630-780	630-780	600-700	650-800	680-830
Mgbatị %		>16	>12	>12	>12	>12	>12	>10
Mbelata%		65-75	60-75	65-75	65-75	65-75	65-75	65-75
Isi ike HB		200-260	200-260	200-260	200-260	200-260	200-260	200-260
Microstructure		Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite