China 0.08mm 0cr25al5 Heating Fecral Resistance Alloy Waya maka Mgbanye Cable Nrụpụta na Factory |TANKII

0.08mm 0cr25al5 Na-ekpo ọkụ Fecral Resistance Alloy Waya maka Igwe ọkụ egosipụtara

0.08mm 0cr25al5 kpo oku Fecral Resistance Alloy Waya maka mgbanye eriri

Nkọwa dị mkpirikpi:

A na-eme FeCrAl alloy site na oke okpomọkụ, iron-chromium-aluminium alloy ferritic nke enwere ike iji na okpomọkụ ruo 1400degrees.Ngwa a na-ahụkarị maka FeCrAl dị ka ihe na-ekpo ọkụ eletrik n'ime ọkụ ọkụ dị elu na ọgwụgwọ okpomọkụ, ceramik, iko, ígwè, na ụlọ ọrụ eletrọnịkị.

Asambodo:ISO 9001

Nha:ahaziri

Ụdị NO.:0Cr25Al5

Resistivity:1.42

Njupụta:7.1 g/cm3

Ihe atụ:N'efu

Nguzogide:283+/-5% ohms/m

Okpomọkụ eji eme ihe kacha elu:1300C

Koodu HS:72230000

Akara ahiaTANKII

Zitere anyị email

Nkọwa ngwaahịa

FAQ

Mkpado ngwaahịa

0.08mm 0cr25al5 kpo oku Fecral Resistance Alloy Waya maka mgbanye eriri

Njirimara:

Na ogologo ndụ ọrụ.Na-ekpo ọkụ ngwa ngwa.High thermal efficiency.Okpomọkụ uniformity.Enwere ike iji kwụ ọtọ.Mgbe a na-eji ya na voltaji a kwadoro, ọ dịghị ihe na-agbanwe agbanwe. Ọ bụ ihe nchebe gburugburu ebe obibi ọkụ ọkụ eletrik.Na ihe ọzọ na ọnụ ahịa nichrome waya.Enwere ike ahaziri dị ka ndị ahịa chọrọ

Ihe e ji mara FeCrAl alloys bụ ezigbo nguzogide oxidation yana ezigbo nkwụsi ike nke na-ebute ndụ mmewere ogologo.

A na-ejikarị ha eme ihe na ọkụ eletrik na ọkụ ụlọ ọrụ na ngwa ụlọ.

Fe-Cr-Al alloy nwere elu resistivity na serviceability okpomọkụ karịa nke NiCr alloy na nwekwara obere price.

Ngwa

A na-eji eriri ihe mgbochi eletriki igwe-chrome-aluminom mee ihe maka ịme ọkụ ọkụ eletrik na ngwa ụlọ na ọkụ ọkụ.Ngwa a na-ahụkarị bụ ígwè dị larịị, igwe na-agba agba, igwe na-ekpo ọkụ mmiri, ihe na-akpụzi rọba na-anwụ anwụ, ígwè ndị na-ere ere, ihe tubular kpuchiri ígwè na ihe katrijị.

mpaghara ngwa

A na-eji ngwaahịa anyị eme ihe na akụrụngwa ọgwụgwọ okpomọkụ, akụkụ akpaaka, ígwè na nchara nchara,

aluminom ụlọ ọrụ, metallurgical akụrụngwa, petrochemical akụrụngwa, iko ígwè, seramiiki ígwè,

igwe nri, igwe ọgwụ, na ụlọ ọrụ injinia ike.

Ọdịnaya kemịkalụ,%

Alloy ihe	Ngwakọta kemịkalụ%
	C	P	S	Mn	Si	Cr	Ni	Al	Fe	ndị ọzọ
	max (≤)				Si	Cr	Ni	Al	Fe	ndị ọzọ
1Cr13Al4	0.12	0.025	0.025	0.7	≤1.00	12.5-15.0	-	3.5-4.5	Zuo ike	-
0Cr15Al5	0.12	0.025	0.025	0.7	≤1.00	14.5-15.5	-	4.5-5.3	Zuo ike	-
0Cr25Al5	0.06	0.025	0.025	0.7	≤0.60	23.0-26.0	≤0.60	4.5-6.5	Zuo ike	-
0Cr23Al5	0.06	0.025	0.025	0.7	≤0.60	20.5-23.5	≤0.60	4.2-5.3	Zuo ike	-
0Cr21Al6	0.06	0.025	0.025	0.7	≤1.00	19.0-22.0	≤0.60	5.0-7.0	Zuo ike	-
0Cr19Al3	0.06	0.025	0.025	0.7	≤1.00	18.0-21.0	≤0.60	3.0-4.2	Zuo ike	-
0Cr21Al6Nb	0.05	0.025	0.025	0.7	≤0.60	21.0-23.0	≤0.60	5.0-7.0	Zuo ike	Nb tinye0.5
0Cr27Al7Mo2	0.05	0.025	0.025	0.2	≤0.40	26.5-27.8	≤0.60	6.0-7.0	Zuo ike

Isi njirimara teknụzụ nke FeCrAl Alloy:

Ụdị Ngwongwo		1Cr13Al4	1Cr21Al4	0Cr21Al6	0Cr23Al5	0Cr25Al5	0Cr21Al6Nb	0Cr27Al7Mo2
Isi akụrụngwa%	Cr	12.0-12.5	17.0-21.0	19.0-22.0	20.5-23.5	23.0-26.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	2.0-4.0	5.0-7.0	4.2-5.3	4.5-6.5	5.0-7.0	6.0-7.0
	Fe	Nhazi	Nhazi	Nhazi	Nhazi	Nhazi	Nhazi	Nhazi
	Re	Kwesịrị ekwesị	Kwesịrị ekwesị	Kwesịrị ekwesị	Kwesịrị ekwesị	Kwesịrị ekwesị	Kwesịrị ekwesị	Kwesịrị ekwesị
							Mgbakwunye Nb:0.5	Mgbakwunye Mo: 1.8-2.2
Akụkụ kacha.jiri okpomọkụ		950	1100	1250	1250	1250	1350	1400
Ebe mgbaze		1450	1500	1500	1500	1500	1510	1510
Njupụta g/cm3		7.40	7.35	7.16	7.25	7.10	7.10	7.10
Nguzogide μΩ·m,20		1.25± 0.08	1.23 ± 0.06	1.42± 0.07	1.35±0.06	1.45± 0.07	1.45± 0.07	1.53± 0.07
Ike Tensile Mpa		588-735	637-784	637-784	637-784	637-784	637-784	684-784
Ọnụego ndọtị%		16	12	12		12	12	10
Ugboro agbagọ ugboro ugboro				5	5	5	5	5
ebuli ngwa ngwa h/		-			80/1300	80/1300		50/1350
Okpomọkụ a kapịrị ọnụ J/g.		0,490	0,490	0,520	0,460	0,494	0,494	0,494
Ọnụọgụ njikwa ọkụ KJ/Mh		52.7	46.9	63.2	60.1	46.1	46.1	45.2
Ọnụọgụ mgbasawanye Linear aX10-6/ (20-1000)		15.4	13.5	14.7	15.0	16.0	16.0	16.0
Isi ike HB		200-260	200-260	200-260	200-260	200-260	200-260	200-260
Microstructure		Ferritic	Ferritic	Ferritic	Ferritic	Ferritic	Ferritic	Ferritic
Magnetik		Magnetik	Magnetik	Magnetik	Magnetik	Magnetik	Magnetik	Magnetik