Tankii44/CuNi44/NC050/6J40 Mgbochi Mgbochi Kasị Elu

Nkọwa dị mkpirikpi:

Aha ngwaahịa:CuNi44 eriri

Ngwakọta kemịkalụ (wt%):Cu: 55.0-57.0%; Ni: 43.0-45.0%; Fe: ≤0.5%; Nna: ≤1.0%; Si: ≤0.1%; C: ≤0.05%

Oke Ọkpụrụkpụ:0.01mm - 2.0mm

Oke obosara:5mm - 600mm

Nhọrọ iwe:Dị nro (annealed), Ọkara-ike, siri ike (oyi tụgharịa)

Ike ọdụdọ:Nrọ: 450-500 MPa; Ọkara-ike: 500-550 MPa; Ike: 550-600 MPa

Ike Mpụta:Nrọ: 150-200 MPa; Ọkara-ike: 300-350 MPa; Ike: 450-500 MPa

Mgbatị (25°C):Nrọ: ≥25%; Ọkara-ike: 15-20%; Ike: ≤10%

Zitere anyị email

Nkọwa ngwaahịa

FAQ

Mkpado ngwaahịa

Nkọwa ngwaahịa

CuNi44 eriri

Nchịkọta ngwaahịa

CuNi44 warara, Ngwongwo ọla kọpa-nickel na-arụ ọrụ dị elu nke Tankii Alloy Material mepụtara ma rụpụta ya, na-egosipụta ọdịnaya nke nickel ọnụ nke 44% na ọla kọpa dị ka metal ntọala. N'iji teknụzụ ọgbara ọhụrụ anyị na-agbagharị oyi na nke ziri ezi, nke a na-enweta nnabata nke akụkụ yana njirimara ihe na-agbanwe agbanwe n'ofe ogbe. Ọ na-ejikọta nkwụsi ike nkwụsi ike eletrik pụrụ iche, nguzogide corrosion dị elu, yana ezigbo nhazi - na-eme ka nguzozi zuru oke maka ngwa eletriki ziri ezi, ihe mmetụta, na ngwaike ụlọ ọrụ na-achọ ntụkwasị obi ogologo oge. Dị ka ngwaahịa flagship na Pọtụfoliyo Alloy Sịpịtị Huona, ọ na-eme ka alloys ọla kọpa dị ala karịa na nkwụsi ike ka ọ na-ejigide arụmọrụ ọnụ maka nnukwu ngwa.

Ụkpụrụ ọkọlọtọ

Alloy ọkwa: CuNi44 (ọla kọpa-Nickel 44)
Nọmba UNS: C71500
Ụkpụrụ Mba Nile: Na-akwado DIN 17664, ASTM B122, na GB/T 2059
Ụdị: Mpempe ewepụghị ewepụghị (profaịlụ omenala dị ma a rịọ ya)
Onye nrụpụta: Tankii Alloy Material, nke enyere ISO 9001 na RoHS maka ịdị mma na nnabata gburugburu.

Uru ndị dị mkpa (vs. Alloys ndị yiri ya)

CuNi44 strip pụtara na ezinụlọ ọla kọpa-nickel alloy maka uru arụmọrụ ezubere iche:

Ultra-Stable Electric Resistance: Resistivity nke 49 ± 2 μΩ · cm na 20 ° C na obere okpomọkụ ọnụọgụ nke nguzogide (TCR: ± 40 ppm / ° C, -50 ° C ka 150 ° C) - dị elu karịa CuNi30 (TCR ± 50 ppm / ° C) na ọla kọpa dị ọcha, na-eme ka ihe mgbochi na-eguzogide obere ihe.
Nguzogide nrụrụ dị elu: Na-eguzogide corrosion ikuku, mmiri dị ọcha na gburugburu kemịkalụ dị nro; na-agafe ule ịgba nnu nnu 1000-hour ASTM B117 na oxidation na-adịghị mma, na-arụ ọrụ ọla na ọla na ntọala ụlọ ọrụ siri ike.
Ọdịmma dị oke mma: ductility dị elu na-enyere aka ịtụgharị oyi ka ọ bụrụ ihe dị mkpa (0.01mm) yana stampụ dị mgbagwoju anya (dịka ọmụmaatụ, grids resistor, mkpachị sensọ) na-enweghị mgbawa-nwere ike ịrụ ọrụ karịa ibe alloy siri ike dị ka CuNi50.
Ngwongwo Mechanical Balanced: Ike nkwụsi ike nke 450-550 MPa (annealed) na elongation ≥25% na-emekọrịta n'etiti nkwụsi ike nhazi na nhazi nhazi, dabara adaba maka ma ibu na-ebu na nkenke-machied components.
Ịdị ọnụ ahịa dị irè: Na-enye arụmọrụ tụnyere metal alloys dị oké ọnụ ahịa (dịka ọmụmaatụ, manganin) na ọnụ ala dị ala, na-eme ka ọ dị mma maka akụkụ ọkụ ọkụ nke a na-emepụta nke ọma.

Nkọwa nka nka

Njirimara	Uru (Ọkachamara)
Ngwakọta kemịkalụ (wt%)	Cu: 55.0-57.0%; Ni: 43.0-45.0%; Fe: ≤0.5%; Nna: ≤1.0%; Si: ≤0.1%; C: ≤0.05%
Oke oke	0.01mm - 2.0mm (nchịkwa: ± 0.0005mm maka ≤0.1mm; ± 0.001mm maka> 0.1mm)
Oke obosara	5mm - 600mm ( ndidi: ± 0.05mm maka ≤100mm; ± 0.1mm maka> 100mm)
Nhọrọ iwe	Dị nro (annealed), Ọkara-ike, siri ike (oyi tụgharịa)
Ike ọdụdọ	Nrọ: 450-500 MPa; Ọkara-ike: 500-550 MPa; Ike: 550-600 MPa
Mpụta Ike	Nrọ: 150-200 MPa; Ọkara-ike: 300-350 MPa; Ike: 450-500 MPa
Mgbatị (25°C)	Nrọ: ≥25%; Ọkara-ike: 15-20%; Ike: ≤10%
Isi ike (HV)	Nrọ: 120-140; Ọkara-ike: 160-180; Ike: 200-220
Nguzogide (20°C)	49 ± 2 μΩ·cm
Nrụpụta okpomọkụ (20°C)	22 W/ (m·K)
Oke okpomoku na-arụ ọrụ	-50°C ruo 300°C (iji na-aga n'ihu)

Nkọwapụta ngwaahịa

Ihe	Nkọwapụta
Emecha elu elu	Annealed na-egbuke egbuke (Ra ≤0.2μm), matte (Ra ≤0.8μm), ma ọ bụ a na-egbu maramara (Ra ≤0.1μm)
Ịdị nro	≤0.05mm/m (maka ọkpụrụkpụ ≤0.5mm); ≤0.1mm/m (maka ọkpụrụkpụ>0.5mm)
Ịrụ ọrụ	Ọ dị mma (dakọtara na ịcha CNC, stamping, na-ehulata na etching)
Weldability	Kwesịrị ekwesị maka ịgbado ọkụ na TIG/MIG (ụdị nkwonkwo na-eguzogide corrosion)
Nkwakọ ngwaahịa	Vacuum-mechiri na akpa mgbochi oxidation na desiccants; spools osisi (maka mpịakọta) ma ọ bụ katọn (maka mpempe akwụkwọ)
Nhazi	Ịkwasa ka obosara dị warara (≥5mm), ibe-ibe ruo ogologo, iwe pụrụ iche, ma ọ bụ mkpuchi mgbochi.

Ngwa a na-ahụkarị

Ngwa eletrọnịkị: ndị na-emegide wirewound ziri ezi, shunts dị ugbu a na ihe ndị nwere ike ime—dị oke mkpa maka mita ike na akụrụngwa mmezi.
Sensọ & Ngwa: grids nlele, ihe mmetụta okpomọkụ, na ndị ntụgharị nrụgide (nkwụsi ike kwụsiri ike na-achọpụta izi ezi nha).
Akụrụngwa ụlọ ọrụ: obere vidiyo na-eguzogide corrosion, ọnụ ọnụ na njikọ maka mmiri, kemịkalụ, na sistemụ HVAC.
Ngwa ahụike: Ngwa ndị dị ntakịrị na akụrụngwa nyocha yana ihe mmetụta wearable (bioc dakọtara na mgbochi corrosion).
Aerospace & Automotive: Igwe ọkụ na-ekpo ọkụ na-adịghị ike na kọntaktị eletrik na avionics na usoro njikwa ụgbọ ala eletrik.

Tankii Alloy Material na-arụ ọrụ njikwa mma siri ike maka eriri CuNi44: batch ọ bụla na-enweta nyocha kemịkalụ XRF, nnwale akụrụngwa (tensile, hardness), na nyocha akụkụ (micrometry laser). Ihe nlele efu (100mm × 100mm) na akụkọ nnwale ihe (MTR) dị mgbe a rịọrọ ya. Ndị otu ọrụ nka na-enye nkwado ahaziri ahazi-gụnyere nhọrọ iwe maka stampụ, njikarịcha nrụnye, yana ndụmọdụ nchekwa corrosion-iji nyere ndị ahịa aka ịbawanye arụmọrụ CuNi44 na ngwa ha.

Nke gara aga: Ultra – Mkpa n’ime – ngwaahịa CuNi44 Foil 0.0125mm ọkpụrụkpụ x 102mm obosara elu nkenke & nguzogide corrosion

Osote: Ọrụ kpo oku nke Ni80Cr20 Nichrome Waya na-eme ka arụmọrụ dị mma

Dee ozi gị ebe a ziga anyị ya