Tebụl 1 Igwe
Eilement | C≤ | P 30 | S≤ | Mn | Si | Cu | Mo | Ni | E |
Ihe mejupụtara% | 0.03 | 0.02 | 0.02 | 0.6-1.1 | 0.3-0.5 | 0.20 | 3.8-4.1 | 78.5-80.0 | Nchetara |
Ndetu:
Ọdịdị na akụkụ nke alloys na-agbaso GBN198-88
Tebụl 2 chọrọ
Aku | Resistivity (μωm) | Dessinty (g / cm3) | Currie isi.c | Etulite tere aka di elu magleto-stracration cofienthθ / 10-6 |
Baa uru | 0.55 | 8. 8.6 | 450 | 2 |
Isiokwu 3 AC magnetiki anụ maka warara (min uru)
Okpurukpu | Ọnụ ọgụgụ dị elu maka ume magnetik bụ 0.1a / m, n'okpuru obere oge dị iche iche na-adịghị mma | |||
60Hz | 400hz | 1KHZ | 10KZ | |
0.02 | 17.5 | 12.5 | ||
0.05 | 18.8 | 9.4 | ||
0.10 | 22.5 | 15 | ||
0.20 | 12.5 | 7.5 | ||
0.35 | 25 | 8. 8.8 |
Tebụl 4 ọnụọgụ nke mgbasawanye nke Linear na Ọnọdụ Ọnọdụ / (X10-6)
Team | 20-100 Celsius C | 20-200ºC | 20-300ºC | 20-400-2C | 20-500ºC | 20-600ºC | 20-700ºC |
Baa uru | 1.3-10.8 | 10.9-11.2 | 14.4-12.9 | 11.9-12.5 | 12.3-13.2 | 12.7-13.4 | 13.1-13.6 |
Tebụl 5 magnetik chọrọ (Clep Flock)
Ọkwa m
(Δ & d) / mm | μ08 / (MHM) ≥ | μm (mhm) ≥ | Bs / t | HC (a / m) ≤ |
0.005 | 12.5 | 44.0 | 0.75 | 6.4 |
0.01 | 17.5 | 87.5 | 0.75 | 4.8 |
0.02-0.04 | 20.0 | 112.5 | 0.75 | 4.0 |
0.05-0.09 | 22.5 | 137.5 | 0.75 | 2.8 |
0.10-0.19 | 25.0 | 162.5 | 0.75 | 2.0 |
0.20-0.34 | 28.0 | 225.0 | 0.75 | 1.6 |
0.35-1.00 | 30.0 | 250.0 | 0.75 | 1.2 |
1.10-2.50 | 27.5 | 225.0 | 0.75 | 1.6 |
2.50-3.00 | 26.3 | 187.5 | 0.75 | 2.0 |
Klas nke ii
(Δ & d) / mm | μ08 / (MHM) ≥ | μm (mhm) ≥ | Bs / t | HC (a / m) ≤ |
0.02-0.04 | 22.5 | 125.0 | 0.75 | 2.4 |
0.05-0.09 | 25.0 | 150.0 | 0.75 | 2.0 |
0.10-0.19 | 27.5 | 187.5 | 0.75 | 1.6 |
0.20-0.34 | 31.3 | 250.0 | 0.75 | 1.2 |
0.35 | 32.5 | 275.0 | 0.75 | 0.79 |
Ọkwa nke III
(Δ & d) / mm | μ08 / (MHM) ≥ | μm (mhm) ≥ | Bs / t | HC (a / m) ≤ |
0.01 | 25.0 | 150.0 | 0.73 | 2.4 |
0.02-0.04 | 31.0 | 190.0 | 0.73 | 1.6 |
0.05-0.09 | 38.0 | 250.0 | 0.73 | 1.2 |
0.10-0.19 | 38.0 | 250.0 | 0.73 | 1.2 |
0.20-0.34 | 38.0 | 280 | 0.73 | 1.0 |
0.35 | 44.0 | 310.0 | 0.73 | 1.0 |
Flally na-ekpo ọkụ (na-echefu) Flastspring
(Δ & d) / mm | μ08 / (MHM) ≥ | μm (mhm) ≥ | Bs / t | HC (a / m) ≤ |
3-22 | 25.0 | 6.5 | 0.75 | 2.4 |
Igwe ọkụ na-ekpo ọkụ (echefu) mmanya
(Δ & d) / mm | μ08 / (MHM) ≥ | μm (mhm) ≥ | Bs / t | HC (a / m) ≤ |
8-100 | 25.0 | 125.0 | 0.75 | 2.4 |