Waya na-eguzogide okpomọkụ HN-AF, ø1-8.0 mm, ruo 1400°C
TKYZngwaahịa bụ ngwaahịa ọhụrụ emepụtara mgbe ngwaahịa TK1 gasịrị, bụ nke ejirila na elu okpomọkụ eletriki kpo oku alloy ihe na-adịbeghị anya. E jiri ya tụnyere TK1, ịdị ọcha ya na-emewanyewanyewanye ma na-emeziwanye nguzogide oxidation ya. Site na ngwakọta ihe pụrụ iche nke ụwa na-adịghị ahụkebe na usoro nrụpụta ọla pụrụ iche, ndị ahịa ụlọ na ndị mba ọzọ achọpụtala ihe ahụ n'ọhịa nke oke okpomọkụ na eriri na-eguzogide okpomọkụ. Ngwa na-aga nke ọma na seramiiki sintering, ọkụ mgbasa ozi, ụlọ ọrụ mmepụta ihe na njupụta ike dị elu na okpomọkụ dị elu.
Isi kemikal na ihe onwunwe
| Properties \ Ọkwa |
|
|
|
| TKYZ |
| ||||
|
| Cr | Al |
| C | Si | |||||
| 20-23 | 5.8 |
| ≤0.04 | ≤0.4 | ||||||
| Okpomọkụ ọrụ na-aga n'ihu (ºC) |
| 1425 | ||||||||
| Nguzogide 20ºCμ.Ω.m) |
|
|
| 1.45 |
| |||||
|
| Njupụta (g/cm3) |
|
|
|
| 7.1 |
| |||
| TensileSike(N/mm²) |
|
|
| 650-800 |
| |||||
|
| Mgbatị (%) |
|
|
|
| >14 |
| |||
| HighTeze ukwuSike(MPa) na 1000℃ |
|
|
| 20 |
| |||||
| ngwa ngwa na 1350 ℃ |
|
| Karịrị80 awa | |||||||
|
|
|
|
|
|
|
|
| |||
| NkeEmissivityOf The FullyOxidizedStee |
|
|
| 0.7 |
| |||||
Nkezi ọnụọgụ mgbasawanye Linear
| Okpomọkụ ℃ | Nkezi ọnụọgụ mgbasawanye ọkụ × 10-6/k |
| 20-250 | 11 |
| 20-500 | 12 |
| 20-750 | 14 |
| 20-1000 | 15 |
| 20-1200 | - |
| 20-1400 | - |
Nrụpụta okpomọkụ
|
| 20 ℃ | 600 ℃ | 800 ℃ | 1000 ℃ | 1200 ℃ | 1400 ℃ |
| Wm-1k-1 | 13 | 20 | 22 | 26 | 27 | 35 |
Ihe mgbazi okpomọkụ na-eguzogide
| Okpomọkụ ℃ | 700 | 900 | 1100 | 1200 | 1300 |
| Ct | 1.02 | 1.03 | 1.04 | 1.04 | 1.04 |