Cuni 23 Na-ekpo ọkụ Alloy Waya na Ngwọta Dị Mma na Stable
Aha ndị nkịtị:CuNi23Mn, NC030, 2.0881
Ọla kọpa nickel alloy wayabụ ụdị waya ejiri ọla kọpa na nickel mee.
A maara ụdị waya a maka nnukwu nguzogide corrosion na ikike ya iguzogide oke okpomọkụ.
A na-ejikarị ya na ngwa ebe ihe ndị a dị mkpa, dị ka na gburugburu mmiri, wiwi eletrik, na usoro kpo oku. Njirimara kpọmkwem nke ọla kọpa nickel alloy waya nwere ike ịdịgasị iche dabere na ihe mejupụtara ya, mana a na-ewerekarị ya dị ka ihe na-adịgide adịgide na ntụkwasị obi maka ọtụtụ ngwa.

Ọdịnaya kemịkalụ,%
| Ni | Mn | Fe | Si | Cu | Ndị ọzọ | Ntuziaka ROHS | |||
| Cd | Pb | Hg | Cr | ||||||
| 23 | 0.5 | - | - | Bal | - | ND | ND | ND | ND |
Njirimara arụrụ arụ nke CuNi23 (2.0881)
| Oke ọrụ na-aga n'ihu | 300ºC |
| Resistivity na 20ºC | 0.3±10% ohm mm2/m |
| Njupụta | 8.9g/cm3 |
| Nrụpụta okpomọkụ | <16 |
| Ebe mgbaze | 1150ºC |
| Ike tensile, N/mm2 Annealed, Dị nro | > 350 Mpa |
| elongation(anneal) | 25% (nkeji) |
| EMF vs Cu, μV/ºC (0 ~ 100ºC) | -34 |
| Ihe onwunwe magnetik | Mba |