FeCrAl ocr23al5 dị elu na-eguzogide ikpo ọkụ maka ọkụ
FeCrAl ocr23al5 kpo oku dị eluwararammewere maka ọkụ ọkụ
| Ọkwa | 0Cr23Al5 |
| Nha | ọkpụrụkpụ: 0.05-3mm obosara: 4-250mm |
| Elu | na-egbuke egbuke sliting |
| Ibu | 1-3kg / mpịakọta, dị ka ndị ahịa' ibu |
| Nguzogide | 1.3±0.05μΩ.m |
| Isi ike (HV) | 180-210HV |
| Ogologo oge | ≥16% |
Ụgwọ nke ụlọ ọrụ Shanghai Tankii Alloy Material Co., Ltd. lekwasị anya na mmepụta nke nichrome alloy, thermocouple waya, fecral alloy, nkenke alloy, ọla kọpa nickel alloy, thermal ịgba alloy wdg n'ụdị waya, mpempe akwụkwọ, teepu, warara, mkpanaka na efere.
Anyị na-ama nwetara ISO 9001 àgwà usoro akwụkwọ na ihu ọma nke ISO 14001 gburugburu ebe obibi nchebe system.We nwe a zuru ezu set nke elu mmepụta eruba nke refining, oyi mbelata, ịbịaru na okpomọkụ ọgwụgwọ wdg Anyị na-anya isi nwere onwe R & D ikike.
| Ọkwa | Ọnọdụ okpomọkụ kachasị elu | Nguzogide | Isi ike | Ike ọdụdọ | Ogologo oge |
| 0Cr13Al4 | 1050 ℃ | 1.25±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr15Al5 | 1100 ℃ | 1.3±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr21Al6Nb | 1300 ℃ | 1.42±0.05μΩ.m | 200-240HV | 750N/mm2 | ≥12 |
| Cr20Ni80 | 1200 ℃ | 1.09±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr15Ni60 | 1150 ℃ | 1.12±0.05μΩ.m | 175-210HV | 750N/mm2 | ≥20 |
| Cr20Ni35 | 1100 ℃ | 1.04±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr25Ni20 (310S) | 1100 ℃ | 0.86±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Ọkwa | Ngwakọta kemịkalụ% | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| ≤ | |||||||||
| 0Cr15Al5 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | itule |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | itule |
| 0Cr13Al4 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | itule |
| Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | itule | 0.5 | ≤1.0 |
| Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | 0.5 | itule |
| Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | - | itule |
| Cr25Ni20 | 0.08 | 0,045 | 0.03 | 2.0 | 0.4-0.6 | 24-26 | 19-22 | - | itule |