Ụlọ ọrụ mmepụta ihe na China Constantan Alloy Heating Waya (6j40) nwere nrụpụta na ụlọ ọrụ mmepụta ihe dị elu

Waya Okpomọkụ Constantan Alloy (6j40) nke Ụlọ Ọrụ Mmepụta Ihe Nwere Foto A Na-egosipụta nke Ọma

Waya Okpomọkụ Constantan Alloy (6j40) nke nwere Ogo Dị Elu

Nkọwa Dị Mkpirikpi:

Waya Constantan nwere nguzogide dị ala na obere okpomọkụ coefficent nke nguzogide yana nguzogide dị larịị/ọnọdụ okpomọkụ n'elu oke sara mbara karịa "manganins". Constantan na-egosikwa nguzogide nchara ka mma karịa man ganinins. Ojiji ya na-abụkarị naanị na sekit ac. Waya Constantan bụkwa ihe na-adịghị mma nke ụdị J thermocouple yana Iron bụ nke dị mma; a na-eji ụdị J thermocouples eme ihe na ngwa ọgwụgwọ okpomọkụ. Ọzọkwa, ọ bụ ihe na-adịghị mma nke ụdị T thermocouple nwere OFHC Copper nke dị mma; a na-eji ụdị T thermocouples na okpomọkụ cryogenic.

Zitere anyị ozi-e

Nkọwa Ngwaahịa

Ajụjụ Ndị A Na-ajụkarị

Akara Ngwaahịa

Waya Okpomọkụ Constantan Alloy (6j40) nke nwere Ogo Dị Elu

Nkọwa Ngwaahịa
Waya Constantan nwere nguzogide dị ala na obere nguzogide okpomọkụ, yana nguzogide dị larịị/ọnọdụ okpomọkụ n'ofe oke karịa "manganins". Constantan na-egosikwa nguzogide nchara ka mma karịa man ganinins. Ojiji ya na-adịkarị naanị na sekit ac.
Waya Constantan bụkwa ihe na-adịghị mma nke ụdị J thermocouple, ebe Iron bụ ihe dị mma; a na-eji ụdị J thermocouple eme ihe n'oge ọgwụgwọ okpomọkụ. Ọzọkwa, ọ bụ ihe na-adịghị mma nke ụdị T thermocouple nwere OFHC Copper nke dị mma; a na-eji ụdị T thermocouple eme ihe n'oge okpomọkụ dị egwu.

Ọdịnaya Kemịkalụ, %

Ni	Mn	Fe	Si	Cu	Ndị ọzọ	Ntuziaka ROHS
						Cd	Pb	Hg	Cr
44	1.50%	0.5	-	Bọọl	-	ND	ND	ND	ND

Njirimara Mekaniki

Oke Ọrụ Na-aga n'ihu	400ºC
Nguzogide na 20ºC	0.49±5%ohm mm2/m
Njupụta	8.9 g/cm3
Ọgbakọ okpomọkụ	-6 (Max)
Ebe Mgbaze	1280ºC
Ike nrụgide, N/mm2 Ejiri ya mee ihe, dị nro	340~535 Mpa
Ike nrụgide, N/mm3 Oyi Akpọgharị	680~1070 Mpa
Ogologo oge (anneal)	25% (Nkeji)
Elongation (oyi kpọchiri akpọchi)	≥Mpempe)2% (Mpempe)
EMF vs Cu, μV/ºC (0 ~ 100ºC)	-43
Nhazi Micrographic	austenit
Njirimara Magnetik	Ọ bụghị