Constantan Flat Waya Copper Nickel Alloy 6j40 Ribbon 0.4*2mm Mmepụta na Ụlọ Ọrụ

Constantan Flat Waya Copper Nickel Alloy 6j40 Ribbon 0.4*2mm Foto a egosipụtara

Constantan Flat Waya Nickel Alloy Copper 6j40 Ribbon 0.4*2mm

Nkọwa Dị Mkpirikpi:

Constantan Flat Waya Nickel Alloy Copper 6j11 Ribbon 0.4*2mm

Resistivity (200C μ Ω. m): 0.1
Oke okpomọkụ ọrụ (0C):200
Ike nrụgide (Mpa):≥ 250
Ebe agbaze (0C):1095
Njupụta (g/cm3):8.9
TCR x10-6/ 0C (20~600 0C): <100

Asambodo:ISO 9001

Nha:Emebere nke ọma

aha ngwaahịa:Alloy Nickel Copper 6j11

ngwa:ụlọ ọrụ

ihe:alloy

atụmatụ:nnukwu iguzogide

ọrụ:ezigbo nkwụsi ike ụdị

ibu:dabere na

nha:dịka ihe onye ahịa chọrọ

agba:aja aja

ọdịdị:waya

MOQ:20kg

Zitere anyị ozi-e

Nkọwa Ngwaahịa

Ajụjụ Ndị A Na-ajụkarị

Akara Ngwaahịa

Waya Constantan dị larịị ọhụrụ nke ọla kọpa Nickel Alloy 6j11 Ribbon 0.4*2mm

Njirimara	Nguzogide (200C μΩ .m)	Oke okpomọkụ ọrụ (0C)	Ike nrụgide (Mpa)	Ebe agbaze (0C)	Njupụta (g/cm3)	TCR x10-6/ 0C (20~600 0C)	EMF vs Cu (μ V/ 0C) (0 ~ 100 0C)
Aha Alloy
NC003 (CuNi1)	0.1	200	≥ 250	1095	8.9	<100	-12

Njirimara Anụ Ahụ	Metric	Okwu ndị mmadụ na-ekwu
Njupụta	8.94 g/cc
Njirimara Mekaniki	Metric	Okwu ndị mmadụ na-ekwu
Ike nrụgide, Kasị Elu	262 – 531 MPa
Ike nrụgide, Mmụba	276 – 524 MPa	Dabere na mmetụta uche
Ogologo oge na ezumike	46.0%	na 50.8 mm.
Modulu nke Elasticity	115 GPA
Oke Poissons	0.310	Agụọla ya
Nhazi ọrụ	Pasentị iri abụọ	UNS C36000 (ọla nchara na-egbutu n'efu) = 100%
Shear Modulus	44.0 GPA
Njirimara Ọdụdọ Eletriki	Metric	Okwu ndị mmadụ na-ekwu
Nguzogide Ọdụdọ Eletriki	0.0000120 ohm-cm @Okpomọkụ 20.0 ° C
Njirimara nke okpomọkụ	Metric	Okwu ndị mmadụ na-ekwu
CTE, ahịrị kwụ ọtọ	17.5 µ m/m-° C @Okpomọkụ 20.0 – 300 Celsius
Ike Okpomọkụ Pụrụ Iche	0.380 J/g-° C
Ọgbakọ okpomọkụ	64.0 W/mK @Okpomọkụ 20.0 ° C
Ebe Mgbaze	< = 1125 ° C	Liquidus
Liquidus	1125 Celsius
Njirimara Nhazi	Metric	Okwu ndị mmadụ na-ekwu
Okpomọkụ Ịkpọchi	565 – 815 Celsius
Okpomọkụ Na-ekpo Ọkụ n'Ọrụ	815 – 950 Celsius
Njirimara nke ihe mejupụtara ya	Metric	Okwu ndị mmadụ na-ekwu
Kọpa, Cu	> = 91.2%
Ígwè, Fe	1.30 – 1.70%
Onye ndu, Pb	< = 0.050%
Manganese, Mn	0.30 – 0.80%
Nickel, Ni	4.80 – 6.20%
Zinc, Zn	< = 1.0%

Ọdịnaya kemịkalụ CuNi44, %

Ni	Mn	Fe	Si	Cu	Ndị ọzọ	Ntuziaka ROHS
						Cd	Pb	Hg	Cr
44	1%	0.5	-	Bọọl	-	ND	ND	ND	ND

Njirimara Mekaniki

Oke Ọrụ Na-aga n'ihu	400ºC
Nguzogide na 20ºC	0.49±5%ohm mm2/m
Njupụta	8.9 g/cm3
Ọgbakọ okpomọkụ	-6 (Max)
Ebe Mgbaze	1280ºC
Ike nrụgide, N/mm2 Ejiri ya mee ihe, dị nro	340~535 Mpa
Ike nrụgide, N/mm3 Oyi Akpọgharị	680~1070 Mpa
Ogologo oge (anneal)	25% (Nkeji)
Elongation (oyi kpọchiri akpọchi)	≥Mpempe)2% (Mpempe)
EMF vs Cu, μV/ºC (0 ~ 100ºC)	-43
Nhazi Micrographic	austenit
Njirimara Magnetik	Ọ bụghị