Mkpanaka Magnesium AZ31 (ASTM B80-13 / DIN EN 1753) maka Anode àjà & Ngwa ụlọ ọrụ

Nkọwa dị mkpirikpi:


  • Aha ngwaahịa:AZ31 Magnesium mkpanaka
  • Ike mpụta (MPa):165
  • Ike nkwụsịtụ, (MPa):245
  • Mgbatị (pasent): 12
  • Ihe mejupụtara (wt. pasent):Mg: Balance; Al: 2.5-3.5%; Zn: 0.7-1.3%; Ọnụ: 0.2-1.0%; Si: ≤0.08%; Fe: ≤0.005%
  • Mmetụta okpomọkụ (25°C):156 W/ (m·K)
  • Oke okpomoku na-arụ ọrụ:-50°C ruo 120°C (iji na-aga n'ihu)
  • Nhọrọ iwe:F (dị ka arụpụtara), T4 (ngwọta-agwọta), T6 (ngwọta-agwọta + agadi)
  • Nkọwa ngwaahịa

    FAQ

    Mkpado ngwaahịa

    Nkọwa ngwaahịa

    AZ31 Magnesium Alloy Bar

    Nchịkọta ngwaahịa

    AZ31 magnesium alloy mmanya, ngwaahịa flagship nke Tankii Alloy Material, bụ mkpanaka magnesium a na-arụ ọrụ dị elu nke emebere maka ngwa nhazi dị fechaa. Ihe mejupụtara magnesium (Mg) dị ka metal ntọala, yana aluminom (Al) na zinc (Zn) dị ka isi ihe na-eme ka ọ bụrụ isi ihe, ọ na-edozi ike ọrụ dị mma, ezigbo ductility, na njupụta dị ala (naanị ~ 1.78 g / cm³ - ihe dịka 35% dị ọkụ karịa alloy aluminum). Ngwakọta a na-eme ka ọ bụrụ ezigbo nhọrọ maka ọla ndị dị arọ na ụlọ ọrụ na-ebute ụzọ mbelata ibu, ebe usoro ọgwụgwọ Huona dị elu na-eme ka ịdị mma na nha nha nha n'ofe niile.

    Ụkpụrụ ọkọlọtọ

    • Alloy Grade: AZ31 (Mg-Al-Zn usoro magnesium alloy)
    • Ụkpụrụ mba ụwa: kwekọrọ na ASTM B107/B107M, EN 1753, na GB/T 5153
    • Ụdị: Ogwe okirikiri (ọkọlọtọ); profaịlụ omenala (square, hexagonal) dị
    • Onye nrụpụta: Tankii Alloy Material, enwetara ISO 9001 maka ogo ọkwa ikuku.

    Uru ndị dị mkpa (vs. Aluminom/Steel Alloys)

    AZ31 magnesium alloy mmanya na-eme ka ihe nhazi ọdịnala na ọnọdụ dị nfe dị oke egwu:

     

    • Ultra-Lightweight: Njupụta nke 1.78 g/cm³, na-enye 30-40% mbelata ịdị arọ ma e jiri ya tụnyere 6061 aluminum na 75% vs. carbon steel-dị mma maka nrụpụta mmanụ ụgbọala na ụgbọ ala / ikuku.
    • Ezi Mechanical Balance: Ike nkwụsi ike nke 240-280 MPa na elongation nke 10-15% (iwe T4), na-egosipụta nguzozi n'etiti ike na nhazi maka ịgbado, igwe na ịgbado ọkụ.
    • Oke nkwụsi ike na ịdị arọ: Specific modulus (E/ρ) nke ~ 45 GPa·cm³/g, karịrị ọtụtụ alloys aluminum maka nkwụsi ike nhazi na okpokolo agba dị fechaa.
    • Nguzogide nrụrụ: Dị ka o kwesịrị, na-etolite oyi akwa oxide nchebe; ọgwụgwọ elu nhọrọ (ntụgharị chromate, anodizing) sitere na Huona na-eme ka iguzogide mmiri na gburugburu ụlọ ọrụ mmepụta ihe.
    • Eco-Enyi na Enyi: 100% nwere ike imegharị ya na obere ume n'oge mmepụta, na-adakọ na ebumnuche nkwado zuru ụwa ọnụ.

    Nkọwa nka nka

    Njirimara Uru (Ọkachamara)
    Ngwakọta kemịkalụ (wt%) Mg: Balance; Al: 2.5-3.5%; Zn: 0.7-1.3%; Ọnụ: 0.2-1.0%; Si: ≤0.08%; Fe: ≤0.005%
    Oke dayameta (Ogwe okirikiri) 5mm - 200mm (nchịkwa: h8 / h9 maka ngwa nkenke)
    Ogologo 1000mm - 6000mm (obere ịkpụ-ruo ogologo dị)
    Nhọrọ iwe F (dị ka arụpụtara), T4 (ngwọta-agwọta), T6 (ngwọta-agwọta + agadi)
    Ike ọdụdọ F: 220-250 MPa; T4: 240-260 MPa; T6: 260-280 MPa
    Mpụta Ike F: 150-180 MPa; T4: 160-190 MPa; T6: 180-210 MPa
    Mgbatị (25°C) F: 8-12%; T4: 12-15%; T6: 8-10%
    Isi ike (HV) F: 60-70; T4: 65-75; T6: 75-85
    Nrụpụta okpomọkụ (25°C) 156 W/ (m·K)
    Oke okpomoku na-arụ ọrụ -50°C ruo 120°C (iji na-aga n'ihu)

    Nkọwapụta ngwaahịa

    Alloy Iwe Ihe mejupụtara (wt. pasent) Njirimara tensile
    Cell efu Cell efu Al Zn Mn Zr Ike mpụta (MPa) Ike ntakiri, (MPa) Ogologo oge

    (pasent)

    AZ31 F 3.0 1.0 0.20 - 165 245 12
    AZ61 F 6.5 1.0 0.15 - 165 280 14
    AZ80 T5 8.0 0.6 0.30 - 275 380 7
    ZK60 F - 5.5 - 0.45 240 325 13
    ZK60 T5 - 5.5 - 0.45 268 330 12
    AM30 F 3.0 - 0.40 - 171 232 12

    Ngwa a na-ahụkarị

    • Automotive: Ngwa ndị dị fechaa (ogidi ndị na-eduzi, okpokolo agba oche, ebe a na-ebufe ihe) iji belata ibu ụgbọ ala ma melite arụmọrụ mmanụ.
    • Aerospace & Defence: Akụkụ nhazi nke abụọ (okpomọkụ ibu ibu, akụkụ ime ụlọ) na ọdụ ụgbọ elu drone, ebe nchekwa oke na-abawanye ikike ịkwụ ụgwọ.
    • Eletrọnịkị ndị ahịa: Laptọọpụ/tablet chassis, igwefoto tripods, na ụlọ ngwá ọrụ ike—ịhazi obere ibu na ịdịte aka.
    • Ngwa ahụike: Ngwa ịwa ahụ dị fechaa na ihe enyemaka ngagharị (oche wheel) maka ịdị mfe nke ojiji.
    • Igwe mmepụta ihe: Akụkụ arụrụ arụ ọrụ ọkụ (conveyor rollers, robotic ogwe aka) iji belata oriri ike n'oge arụ ọrụ.

     

    Tankii Alloy Material na-ahụ maka njikwa mma maka AZ31 magnesium alloy bars, yana batch ọ bụla na-eme nyocha ihe mejupụtara kemịkalụ, nnwale akụrụngwa, yana nyocha akụkụ. Ihe nlele efu (ogologo 100mm-300mm) na akụkọ nyocha ihe (MTR) dị mgbe achọrọ. Ndị otu anyị na-arụ ọrụ na-enyekwa nkwado ngwa ngwa-gụnyere ntuziaka igwe na ndụmọdụ nchebe corrosion-iji nyere ndị ahịa aka ịbawanye arụmọrụ nke AZ31 na ọrụ ha.