Alkrothal 14 ferritic iron chromiumaluminium alloy (FeCrAl alloy)
Alkrothal 14 (waya na-ekpo ọkụ na waya na-eguzogide) Alkrothal 14 bụ ferritic ironchromiumaluminium alloy (FeCrAl alloy) nke nwere nnukwu resisivity kwesịrị ekwesị maka ojiji na okpomọkụ ruo 1100°C (2010°F). A na-ejikarị Alkrothal 14 eme waya na-eguzogide ọkụ eletrik maka ngwa dịka waya na-ekpo ọkụ.
Ihe mejupụtara kemịkalụ
| C% | Si% | Mn% | Cr% | Al% | Fe% | |||||||
| ihe mejupụtara aha | 4.3 | Bọọl | ||||||||||
| Nkeji | - | 14.0 | ||||||||||
| Max | 0.08 | 0.7 | 0.5 | 16.0 |
NGWỌTA MGBE
| nha waya | Ike mmeputa | Ike ọdụdọ | Ogologo | Ike siri ike |
| Ø | Rp0.2 | Rm | A | |
| mm | MPa | MPa | % | Hv |
| 1.0 | 455 | 630 | 22 | 220 |
| 4.0 | 445 | narị isii | 22 | 220 |
| 6.0 | 425 | 580 | 23 | 220 |
MODULUS nke YOUNG
| okpomọkụ°C | 20 | 100 | 200 | narị anọ | narị isii | narị asatọ | 1000 |
| GPA | 220 | 210 | 205 | 190 | 170 | 150 | 130 |
Njirimara mekaniki na okpomọkụ dị elu
| Okpomọkụ °C | 900 |
| MPa | 30 |
Oke mgbanwe ike nrụgide kachasị elu 6.2 x 10 / min
Ike CREEP – 1% N'IME 1000 H
| Okpomọkụ °C | narị asatọ | 1000 |
| MPa | 1.2 | 0.5 |
ÀGWÀ AHỤ́
| Njupụta g/cm3 | 7.28 |
| Ike iguzogide ọkụ eletrik na 20°C Ω mm/m | 1.25 |
| Ọnụọgụ Poisson | 0.30 |
IHE OKPOMỌKỤ NKE NJIKỌRỌ
| Okpomọkụ°C | 100 | 200 | 300 | narị anọ | 500 | narị isii | 700 | narị asatọ | 900 | 1000 | 1100 |
| Ct | 1.00 | 1.02 | 1.03 | 1.04 | 1.05 | 1.08 | 1.09 | 1.10 | 1.11 | 1.11 | 1.12 |
ONYE NA-AGBANWE ỌRỤ ...
| Okpomọkụ °C | Mgbasawanye okpomọkụ x 106/ K |
| 20 - 250 | 11 |
| 20 - 500 | 12 |
| 20 - 750 | 14 |
| 20 - 1000 | 15 |
ỌRỤ ỌKỤ
| Okpomọkụ °C | 20 |
| W/m K | 16 |
Ike Okpomọkụ Pụrụ Iche
| Okpomọkụ°C | 20 | 200 | narị anọ | narị isii | narị asatọ | 1000 |
| kJ n'arọ-1K-1 | 0.46 | 0.63 | 0.72 | 1.00 | 0.80 | 0.73 |