42hxtio 3j53 Stirp Ni Span C902 Mmiri Na-adịgide adịgide Magnetic Alloy Precision Elastic Parts Material Ribbon

Nkọwa dị mkpirikpi:

3J 53 alloy bụ ikiri mmiri na-esi ike nickel-Iron-Chromium alloy nwere ọnụọgụ thermoelastic pụtara ìhè.
àgwà na magburu onwe oxidation iguzogide na elu okpomọkụ ikuku. Enwere ike ịhazi alloy ahụ
inwe modul nke elasticity mgbe niile na okpomọkụ sitere na -45 ruo +65oC (-50 ruo +150oF).


  • Aha ngwaahịa:3J53(C902) Ntughari
  • Ọkwa ngwaahịa:3J53(C902)
  • Isi ihe: Ni
  • Ọmụmaatụ:Nkwado
  • Nhazi:Nkwado
  • Asambodo:ISO9001, RoHs
  • Nkọwa ngwaahịa

    FAQ

    Mkpado ngwaahịa

    42hxtio 3j53 Ni SpanC902 Igwe Igwe Igwe Igwe Igwe Igwe Igwe Igwe Igwe Igwe Igwe Ọdụdọ
    Nkenke ihe Nkeji na-agbanwe agbanwe

    Ọkpụrụkpụ mpempe akwụkwọ: 0.1mm ~ 3.5mm

    Ọkpụrụkpụ efere: 3.5mm ~ 40.0mm
    Ogwe Dia 5.0mm ~ Dia180.0mm

    Pipe OD 120mm ~ 8.0mm, ID 8.0 ~ 129mm

    Waya Dia 0.1mm-Dia5.0mm

    Ngwa Ngwa

    A na-ejikarị ha eme ngwa ngwa, akụkụ ahụ na-agbanwe ikuku, ụda olu, diaphragms.

    Nkọwa

    Nickel-Iron-Chromium alloy nke mmiri ozuzo siri ike nke nwere ọnụọgụ thermoelastic pụtara ìhè.
    àgwà na magburu onwe oxidation iguzogide na elu okpomọkụ ikuku. Enwere ike ịhazi alloy ahụ
    inwe modul nke elasticity mgbe niile na okpomọkụ sitere na -45 ruo +65oC (-50 ruo +150oF).

    Oke
    TABLE 1 Ntụaka Cross

    Aha Contury 1 Aha 2

    Russia 42HXTΙΙ H42XT

    USA Ni-Span c902 Elinvar

    Germany Ni-Span C

    UK Ni-Span C

    Japan Sumispan-3 EL-3

     

    TABLE 2 Chemical chọrọ

    Ihe mejupụtara,%

    C ≤ 0.05

    Si≤ 0.80

    P≤ 0.020

    S≤ 0.020

    Mn≤ 0.80

    Ni≤ 41.5-43.0

    Kr 5.20-5.80

    TI 2.3-2.70

    Al 0.5-0.8

    FE fọdụrụnụ

    ndetu:

    1.The udi na akụkụ nke alloys bụ na nnabata YB/T5256-1993

     

    TABLE 3 chọrọ anụ ahụ

    Ebumnuche Ngwongwo

    Njupụta 8.0

    Modulus nke Elasticity (E/Empa) 176500-191000

    Shear eleasticity(G/MPa) 63500-73500

    Vickers ike (HV) 350-450

    Njupụta nnabata ọnọdụ ọnọdụ (B600/T) 0.7

    Ọnụọgụ ọnụọgụgụ nke Linear Expansion20-100ºC(10-6/K) 8.5

    Resistivity p/(Ω°m) 1.1

     

    TABLE 4 Mpụta Ike (mgbe ọgwụgwọ okpomọkụ gasịrị)

    Ọkpụrụkpụ Steeti Nbunye/mm Ike/Mpa

    Ebichiri 0.50-2.50 <685

    Oyi akpọrela 0.50-1.00>885

     

    TABLE 5 Ọnọdụ okpomọkụ nke modul nke elasticity

    Okpomọkụ ịka nká/ºC Ọnụego okpomọkụ nke modul nke elasticityβE/(10-6/ºC)(-6~+80ºC)

    Oyi Rolling Annealed

    500 -38~15 +18~+12

    550 -22~0 +10~+35

    600 0~+20 +35~+55

    650 0~+20 +42~+64

    700 0~+20 +40~+60

    750 -4~+16 +28~+50

     

    TABLE 6 chọrọ akụrụngwa akụrụngwa

    Ọkpụrụkpụ Steeti Nnyefe Ọdịbe/mm Ike Tensile/MPa Elongationò(%)≥

    Mwepu ewepụrụ 0.20-0.50 <885 20
    Waya oyi adọtara 0.20-3.0>930