Resistohm 145A1 1425 C FECral A1 Kan-thal A1 AF APM Igwe na-eguzogide ọkụ eletrik

Nkọwa dị mkpirikpi:


  • Ụdị NO.:TKYZ
  • Ngwakọta kemịkalụ:FeCr25AL6
  • Okpomọkụ eji eme ihe kacha elu:1425C
  • Njupụta:7.1 g/cm3
  • Resistivity:1.45
  • Mgbatị:20%
  • Nkọwapụta:0.1-10.0mm
  • Akara ahiaTANKII
  • Koodu HS:72230000
  • Mmalite:China
  • Ike mmepụta:Tọn 300 / ọnwa
  • Nkọwa ngwaahịa

    FAQ

    Mkpado ngwaahịa

    Ngwaahịa TKYZ bụ ngwaahịa ọhụrụ emepụtara mgbe ngwaahịa TK1 gasịrị, nke ejirila ọtụtụ ihe na-ekpo ọkụ ọkụ eletrik dị elu na afọ ndị na-adịbeghị anya. E jiri ya tụnyere TK1, ịdị ọcha ya na-emewanyewanyewanye ma na-emeziwanye nguzogide oxidation ya. Site na ngwakọta ihe pụrụ iche nke ụwa na-adịghị ahụkebe na usoro nrụpụta ọla pụrụ iche, ndị ahịa ụlọ na ndị mba ọzọ achọpụtala ihe ahụ n'ọhịa nke oke okpomọkụ na eriri na-eguzogide okpomọkụ. Ngwa na-aga nke ọma na seramiiki sintering, ọkụ mgbasa ozi, ụlọ ọrụ mmepụta ihe na njupụta ike dị elu na okpomọkụ dị elu.

     

    Isi kemikal na ihe onwunwe

     

    Properties \ Ọkwa

    TKYZ

    Cr

    Al

    C

    Si

    20-23

         5.8

    0.04

    0.4

    Okpomọkụ ọrụ na-aga n'ihu (ºC)

    1425

    Resisivity 20ºC (μ.Ω.m)

    1.45

    Njupụta (g/cm3)

    7.1

    TensileSike(N/mm²)

    650-800

    Mgbatị (%)

    >14

    HighTeze ukwuSike(MPa) na 1000℃

    20

    ndụ ngwa ngwa na 1350 ℃

    Karịrị80 awa

    NkeEmissivityOf The FullyOxidizedStee

    0.7

    Nkezi ọnụọgụ mgbasawanye Linear

    Okpomọkụ ℃

    Nkezi ọnụọgụ mgbasawanye ọkụ × 10-6/k

    20-250

    11

    20-500

    12

    20-750

    14

    20-1000

    15

    20-1200

    -

    20-1400

    -

    Nrụpụta okpomọkụ

    50 ℃

    600 ℃

    800 ℃

    1000 ℃

    1200 ℃

    1400 ℃

    Wm-1k-1

    11

    20

    22

    26

    27

    35

    Ihe mgbazi okpomọkụ na-eguzogide

    Okpomọkụ ℃

    700

    900

    1100

    1200

    1300

    Ct

    1.02

    1.03

    1.04

    1.04

    1.04