Ọkọlọtọ: AWS A5.10 ER4043 | Ngwakọta kemịkalụ% | ||||||||||
Si | Fe | Cu | Mn | Zn | Ndị ọzọ | AL | |||||
Ọkwa ER4043 | 4.5-6.0 | ≤ 0.80 | ≤ 0.30 | ≤ 0.05 | ≤ 0.10 | - | Zuo ike | ||||
Ụdị | Spool (MIG) | Tube (TIG) | |||||||||
Nkọwapụta (MM) | 0.8,0.9,1.0,1.2,1.6,2.0 | 1.6,2.0,2.4,3.2,4.0,5.0 | |||||||||
ngwugwu | S100/0.5kg S200/2kg S270, S300/6kg-7kg S360/20kg | 5kg / igbe 10kg / igbe ogologo: 1000MM | |||||||||
Ihe eji arụ ọrụ | Ngwakọta okpomọkụ ºC | Eletriki IACS | Njupụta g/mm3 | Ịkwụsị Mpa | Mmụba Mpa | Ogologo oge % | |||||
575-630 | 42% | 2.68 | 130-160 | 70-120 | 10-18 | ||||||
Dayameta(MM) | 1.2 | 1.6 | 2.0 | ||||||||
MIG ịgbado ọkụ | Welding ugbu a – A | 180-300 | 200-400 | 240-450 | |||||||
Voltage ịgbado ọkụ - V | 18-26 | 20-28 | 22-32 | ||||||||
TIG ịgbado ọkụ | Dayameta (MM) | 1.6-2.4 | 2.4-4.0 | 4.0-5.0 | |||||||
Welding ugbu a – A | 150-250 | 200-320 | 220-400 | ||||||||
Ngwa | Akwadoro maka ịgbado ọkụ 6061,6XXX usoro;3XXXand2XXX usoro aluminum alloy. | ||||||||||
Mara | 1, Ngwaahịa nwere ike idowe ruo afọ abụọ n'okpuru ọnọdụ nke factory mbukota na akara, na Enwere ike iwepụ mbukota maka ọnwa atọ n'okpuru ọnọdụ ikuku na-emekarị. 2, Ngwaahịa kwesịrị ịchekwa na ventilated, nkụ na ebe. 3, Mgbe e wepụrụ waya na ngwugwu, a na-atụ aro na mkpuchi mkpuchi uzuzu kwesịrị ekwesị |
Almunium alloy usoro ịgbado ọkụ:
Ihe | AWS | Aluminom Alloy Chemical Compostition(%) | |||||||||
Cu | Si | Fe | Mn | Mg | Cr | Zn | Ti | AL | |||
Aluminom dị ọcha | ER1100 | 0.05-0.20 | 1.00 | 0.05 | 0.10 | 99.5 | |||||
Plasticity dị mma, maka ịgbado ọkụ gas ma ọ bụ ịgbado ọkụ argon nke aluminom dị ọcha na-eguzogide corrosion. | |||||||||||
Aluminom Alloy | ER5183 | 0.10 | 0.40 | 0.40 | 0.50-1.0 | 4.30-5.20 | 0.05-0.25 | 0.25 | 0.15 | Rem | |
Ike dị elu, ezigbo nguzogide corrosion, maka ịgbado ọkụ argon arc. | |||||||||||
ER5356 | 0.10 | 0.25 | 0.40 | 0.05-0.20 | 4.50-5.50 | 0.05-0.20 | 0.10 | 0.06-0.20 | Rem | ||
Ike dị elu, ezigbo nguzogide corrosion, maka ịgbado ọkụ argon arc. | |||||||||||
ER5087 | 0.05 | 0.25 | 0.40 | 0.70-1.10 | 4.50-5.20 | 0.05-0.25 | 0.25 | 0.15 | Rem | ||
Ezigbo nguzogide corrosion, weldability na plasticity, maka ịgbado ọkụ gas ma ọ bụ ịgbado ọkụ argon. | |||||||||||
ER4047 | 0.30 | 11.0-13.0 | 0.80 | 0.15 | 0.10 | 0.20 | Rem | ||||
tumadi maka brazing na soldering. | |||||||||||
ER4043 | 0.30 | 4.50-6.00 | 0.80 | 0.05 | 0.05 | 0.10 | 0.20 | Rem | |||
Ezigbo nguzogide corrosion, ngwa sara mbara, nchekwa gas ma ọ bụ ịgbado ọkụ argon acr. | |||||||||||
Usoro nickel Welding:
ERNiCrMo-3,ERNiCrMo-4,ERNiCrMo-13,ERNiCrFe-3,ERNiCrFe-7,ERNiCr-3,ERNiCu-7,ERNiCu-7,ERNi-1
Ọkọlọtọ:Dabara na Asambodo AWS A5.14 ASME SFA A5.14
Nha: 0.8MM / 1.0MM / 1.2MM / 1.6MM / 2.4MM / 3.2MM / 3.8MM / 4.0MM / 5.0MM
Ụdị: MIG (15kgs / spool), TIG (5kgs / igbe)