0Cr25Al5 Waya Fecral Alloy Ejiri Mee Ihe n'Ime Ngwa Ihe Na-ekpo Ọkụ Foto A Na-egosipụta
  • 0Cr25Al5 Fecral Alloy Waya eji eme ihe na ngwa ihe na-ekpo ọkụ
  • 0Cr25Al5 Fecral Alloy Waya eji eme ihe na ngwa ihe na-ekpo ọkụ

0Cr25Al5 Fecral Alloy Waya eji eme ihe na ngwa ihe na-ekpo ọkụ

Nkọwa Dị Mkpirikpi:

0Cr25Al5 bụ ihe eji eme ígwè-chromium-aluminium alloy (FeCrAl alloy) nke nwere nnukwu iguzogide, obere ọnụọgụ nke iguzogide eletriki, okpomọkụ ọrụ dị elu, ezigbo iguzogide nchara n'okpuru okpomọkụ dị elu. Ọ dị mma maka ojiji na okpomọkụ ruo 1250°C. A na-eji ngwa ndị a na-ejikarị eme ihe maka 0Cr25Al5 na seramiiki eletrik, ọkụ ụlọ ọrụ mmepụta ihe, na ihe na-ekpo ọkụ.

 


Nkọwa Ngwaahịa

Ajụjụ Ndị A Na-ajụkarị

Akara Ngwaahịa

0Cr25Al5 Fecral Alloy Waya eji eme ihe na ngwa ihe na-ekpo ọkụ

0Cr25Al5 bụ ihe eji eme ka ígwè-chromium-aluminum alloy (FeCrAl alloy) nke nwere nnukwu iguzogide, obere ihe mgbochi eletriki, oke okpomọkụ ọrụ, ezigbo nguzogide nchara n'okpuru oke okpomọkụ. Ọ dị mma maka ojiji na okpomọkụ ruo 1250°C.

A na-eji ngwa ndị a na-ejikarị eme ihe maka 0Cr25Al5 n'elu ihe esi nri seramiiki eletrik, ọkụ ụlọ ọrụ mmepụta ihe, na ihe na-ekpo ọkụ.

Ihe mejupụtara nkịtị%

C P S Mn Si Cr Ni Al Fe Ndị ọzọ
Max
0.06 0.025 0.025 0.70 Oke kachasị 0.60 23.0~26.0 Oke kachasị 0.60 4.5~6.5 Bọl. -

Àgwà Mechanical nkịtị (1.0mm)

Ike mmeputa Ike ọdụdọ Ogologo
Mpa Mpa %
500 700 23

Àgwà anụ ahụ nkịtị

Njupụta (g/cm3) 7.10
Nguzogide eletriki na 20ºC (ohm mm2/m) 1.42
Ọnụọgụ conductivity na 20ºC (WmK) 13

Ọnụọgụ nke mgbasawanye okpomọkụ

Okpomọkụ Ọnụọgụ nke Mgbasawanye Okpomọkụ x10-6/ºC
20 ºC- 1000 ºC 15

Ike okpomọkụ kpọmkwem

Okpomọkụ 20ºC
J/gK 0.46

Ebe agbaze (ºC) 1500
Oke okpomọkụ na-arụ ọrụ na-aga n'ihu na ikuku (ºC) 1250
Njirimara magnetik magnetik

ụlọ akụ foto (5) ụlọ akụ foto (1) ụlọ akụ foto (2) fotobank (9) ụlọ akụ fotobank

  • Nke gara aga:
  • Osote:
    • Dee ozi gị ebe a zitere anyị ya

    Ngwaahịa dị iche iche

    Pịa "Enter" iji chọọ ma ọ bụ "ESC" iji mechie